Izdelki za lončnica iz gline (4)

Osmocem SCK Fiber-reinforced monocomponent cement mortar, based on hydraulic binders, superprogoline fillers, selected fine aggregates and crystallizing reagent agents, which favor the penetration of the compound into the support. Ideal for low-thickness protective coatings (4 to 10 mm), with high counterweight adhesion. The specific formulation makes this product ideal for coatings in aggressive environments in contact with chlorides and sulphates (sewage systems). Packaging: 25 kg bag UM: €/kg

Mezcla de aditivos, condimentos y especias, para la elaboración del producto cárnico no tratado por el calor denominado “Salchichón” o “Chorizo blanco” de calidad “Extra”, elaborado con técnicas de curación lenta (temperatura de 6 a 12ºC y HR inicial del 78 al 86%). Formato: bolsa 4kg

Mezcla de aditivos, condimentos y especias, de uso charcutero, para la elaboración del producto cárnico tratado por el calor denominado “Morcilla”. Formato: bolsa 5kg

Grout CR Composite , castable, anti-washout, controlled shrinkage cement mortar, superfluid consistency, based on high-resistance cements, superpozzolanic fillers (MICROSIL 90), polymeric modifiers, shrinkage resistant agents, specific additives, calcium silicate mineral fibres, selected silica aggregates. - Based on of thickened silica fume - three-dimensionally reinforced fibre with mineral and synthetic fibres - Provides high adherence and adhesion - dimensionally stable (shrinkage-compensated) - Provides high stability-physical chemical and resistance to chlorides and sulphates - suitable for underwater castings: it is anti-washout - high strength in terms of hydrostatic positive and negative thrust. Repair and protective coatings of hydraulic structures, marine and underwater structures, and articles in critical situations: harsh chemical-physical, leaching water, marine atmosphere, etc. Filling of formwork for the containment of cast immersed in sea water. In case of underwater application, the installation operations must be carried out within 8-10 hours of cleaning and "fouling" (accumulation and deposits of organic and inorganic particles on product surfaces) removal. An adequate roughening of the surfaces by scarifying, sandblasting etc. is always necessary in order to obtain the maximum adhesion values to the substrate. The optimal values are obtained with high pressure hydro-scarification. Bare the irons undergoing disruptive oxidation or deeply oxidized, removing the rust of the exposed irons (by sandblasting or abrasive brushes). Pour 2/3 of total mixture water in the cement mixer, gradually add the product and the remaining water, until a homogeneous mixture of the required consistency is obtained. For sizable filling thicknesses, greater than 60 mm, Ghiaietto 6.10 (inert washed is selected with a particle size of from 6-10 mm) can be added in a percentage ranging from 20% to 40 %, on the basis of practical requirements. In some particularly demanding cases in terms of the resistance to the "dry-wet" cycle (for example, for the action of the tides) or for chemical attacks particularly strong, it would be advisable to add, in addition to the gravel, even thickened silica fume(MICROSIL 90), and in a variable amount depending on the thickness and construction-related need, to further improve the waterproofing and the mechanical strength of the product. In these cases, please contact our Technical Service. In the case of casts in water, make sure of perfect product hardening before removal of the formwork. Approximately 20,50 kg/m² of Grout CR for every centimetre of thickness to be implemented (approximately 2050 kg per cubic metre). Packaging: 25 kg bag UM: €/kg